1.2344 Tool Steel. 1.2344 X40CrMoV5-1 BS4659 BH13 is an air hardening hot work tool steel which combines a very good red-hardness with toughness and covers a wide variety of applications. 1.2344 X40CrMoV5 hot work tool steel can be water cooled in service and offers high temperature strength and wear resistance. 1.2344 is one of the hot work, chromium type tool steels. 1.2363 steel barcold work mould steel 1.2363 would be used for good wear resistance suitable and good toughness special tools, such as the widely used materials in blanking die and forming die , eion roll, punches, also used for certain types of shear blade.
1.2343 tool steel is used for highly stressed structural parts such as aircraft landing gear. And it is suitable for high-speed hammer forging molds. Such as aluminum and magnesium alloy hot forging die, and its hardness always is 42-50HRC. Black metal forging molds, hardness is 40-50HRC. ASSAB 23441.1 Mn 0.4 Cr 5.2 Mo 1.4 V 0.9 Standard specification AISI H13, WNr. 1.2344, SKD 61, EN X40CrMoV5-1 Delivery condition Soft annealed to approx. 205 HB. Colour code Orange / Violet GENERAL ASSAB 2344 is a chromium-molybdenumvanadium-alloyed tool steel which is characterised by:z Good resistance to abrasion at both low and high temperatures
VIDAR 1 ESR VIDAR 1 ESR H11 1.2343 SKD 6 UNIMAX UNIMAX CORRAX CORRAX ASSAB 2083 420 1.2083 SUS 420J2 ASSAB 718 HH is a prehardened mould steel, which offers the following benefits:z No hardening risks WELDING Good results when welding tool steel can be achieved China HMD5/CH-1/7crsimnmov Die Steel Material Plate Auto Mold Steel, Tool Steel, Die Steel manufacturer / supplier in China, offering HMD5/CH-1/7crsimnmov Die Steel Material Plate Sheet, Cheap Price D2 1.2379 SKD11 Cr12MOV Xw-41 Xw-42 K110 Alloy Mould Tool Steel Plate Sheet Die Steel, 8407 1.2344 H13 ESR 1.2343 H11 SKD61 W301 W302 W303 Dievar Dac55 Hot Work Alloy Die Tool Metal Steel Round Bar and so on.
Cold Work Steel - MAX STEEL l Special Steels And Metals . Cold Work Steel 1.2826 1.2767 1.2510 SKS3 1.2436 1.2379 Mod SKD11 Mod 1.2363 SKD12 SK5 DIN 1.2367, hot work tool steel,similar to AISI H11,but Basic information about DIN 1.2367. 1.2367 is a choromium -Molybdenum hot work steel that is similar to AISI H11 hot work steel, but which contains a higher molybdenum content, The higher molybdenum gives DIN 1.2367 better hot hardness and temper resistance,along with higher attainable hardness and deeper hardenability than the more common H11 and H13 hot work steels, Typical applications
1234312344 1231212738 1402114034. GB1299 . spring steel. 65Mn55Si2Mn60Si2MnA60Si2CrA60Si2CrVA50CrVA (etc.) GB1222 carbon tool steel. T7T8T9T10T12T8Mn(etc.) GB1298 stainless steel. 1Cr132Cr134Cr131Cr12Mo1Cr11MoV2Cr12NiMo1W1V0Cr17Ni4Cu4Nb (etc.) GB4230 GB8732 Excellence in Special SteelProducts. SH 2363/ A2/ Cr5Mo1V. SH 2714/ L6/ 5CrNiMoV. SH 2343/ H11/ 4Cr5MoSiV. SH 2344/ H13/ 4Cr5MoSiV1. SH 3343/ M2/ W6Mo5Cr4V2.
- IntroductionHeat TreatmentForgingTemperingApplicationsChromium hot-work tool steels are designated as group H steelsaccording to the AISI classification system. This series of steelsstart from H1 to H19. The most commonly used chromium hot-work steelsare H11, H12, and H13, which can be air hardened in 150 mm thicksections. The steels are subjected to minimal distortion duringhardening due to their balanced alloy content. The tools produced fromchromium hot-work steels can be cooled using water without damage asthese steels have low carbon and alloy cEverything You Need To Know About H13 Tool SteelDEKSep 18, 2020 · H13 tool steel in terms of its mechanical properties tends to show a behavior that varies with heat treatment. H13 tool steel records a reduction of area as 50% and modulus of elasticity as 215 GPa at 20 °C. The ranges for tensile strength in terms of ultimate and yield vary as 1000-0 MPa and 1200-1590 MPa respectively.
Hubei Rising Technology Co., LtdRising is a professional mill factory, located in steel base of China---Daye city, mainly producing and supplying of mold steel, alloy steel and tool steel, has been committing itself to offering the best special steel solution to its customers. With the annual producti
Werkstoff 1.2343 DIN 8555 MSG/WSG 3-GZ-55ST. Average Chemical analysis. C% Si% Mn% P% S% Cu% Cr% Ni% Mo% Ti% 0,37:0,40:1,10:0,030:0,020:0,25:7,00:0,20:2,20:0,30:The copper value include the surface coating. Typical mechanical properties of all-weld metal. Hardness Hardness; HB HRC; 540 - 590:52 - 57:The mechanical properties are Mat.No. 1.2345, DIN X50CrVMo51, AISI Approx. H11 - Co., Ltd.Short Description:Designation by Standards Mat. No. DIN EN AISI 1.2345 X50CrVMo51 - Approx. H11 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.51 0.95 0.30 5.00 1.35 - 0.90 - - Description UTOPMO4 is a 5% chromium hot work tool steel designed particularly for applications requiring extreme toughness combined with good red hardness.
RAVNEX DC is a premium tool steel of highest toughness produced in Metal Ravne. Chart shows its toughness at high temperature compared to 1.2343 and conventional W.Nr1.2344 hot-work tool steel. TOUGHNESS Un-notched specimens (7 x 10 x 55 mm3) are Steel & Products Manufacturers, Suppliers & Factory Steel & Products manufacturers & suppliers, China Steel & Products manufacturers, suppliers & factory directory, find Chinese Steel & Products manufacturers, suppliers, factories, exporters and wholesalers easily on Made-in-China.,page8
For deposit welding of Mo-alloyed high-speed steel. Mainteinance and new manufacture of high-speed steel tools. Weld deposit without soft-annealing can only be processed by grinding. To be used for cutting tools, gouges, turning chisel, broaches, taps, twist drills, reamers, milling tools, cold extrusion dies. 57-62 HRC. W.N 1.3348 Vidar 1 ESR Eng 090827 - Uddeholmanalysis % 0.38 1.0 0.4 5.0 1.3 0.4 Standard AISI H11, B H11, W.-Nr. 1.2343, specification EN X37 CrMoV 5-1 Delivery condition Soft annealed to approx.185 HB Colour code Blue/orange HIGH-TEMPERATURE STRENGTH AT ELEVATED TEMPERATURES Heat treatment Soft annealing Protect the steel and heat through to 850°C (1562 °F). Then cool in furnace at 10
WELDING OF TOOL STEEL General informa-tion on welding of tool steel To ol steel contain up to 2.5% carbon as well as alloying elements such as manganese, chromium, molybdenum, tungsten, vanadium and nickel. The main problem in welding tool steel stems from its high hardenability. Welds cool quickly once the heat source is removed and the weld Z38CDV5 (AFNOR NFA ) - Worldwide equivalent - Steel X37CrMoV5-1 (1.2343) , Z38CDV5 (France, AFNOR NFA ) - European (EU, EN) and wordwide Steel equivalent grades. These comparison table is only intended as an indication of the closest khown equivalent grades. The source standarts should always be checked for the specific purpose for each material, in case of doubt.
AISI H11 tool steel is a 5% chromium hot-work tool steel. Otai steel supplies good quality H11 steel, and equivalents 1.2343/X37CrMoV5-1, SKD6, BH11 steel.